Análisis de falla en tubos de latón en contacto con gas licuado de petróleo.
Premature failure of a condenser of an oil refinery was analyzed in order to determine its cause. A liquid petroleum gas polluted with ammonia and sulfides and cyanides ions flows outside of these tubes visual inspection in the fault zone showed cracks in circumferential direction of the tube and cl...
| Publicado en: | Revista CENIC Ciencias Quimicas Vol. 44; no. 1; pp. 49 - 57 |
|---|---|
| Autores principales: | , , , , |
| Formato: | Artículo |
| Publicado: |
Centro Nacional de Investigaciones Cientificas
2013
|
| Materias: | |
| Acceso en línea: | Ver este registro en EBSCOhost |
| fields | @attributes: recordID: 1 pdfLink: plink: https://search.ebscohost.com/login.aspx?direct=true&db=lth&AN=110712598&site=ehost-live header: @attributes: shortDbName: lth uiTerm: 110712598 longDbName: MedicLatina uiTag: AN controlInfo: bkinfo: jinfo: jid: 10158553 UF0 jtl: Revista CENIC Ciencias Quimicas issn: 10158553 maglogo: N pubinfo: dt: 2013 vid: 44 iid: 1 pid: 21205 pub: Centro Nacional de Investigaciones Cientificas artinfo: ui: 110712598 ppf: 49 ppct: 8 formats: fmt: @attributes: type: P size: 899KB tig: atl: Análisis de falla en tubos de latón en contacto con gas licuado de petróleo. aug: au: Rivera-Beltrán, Yichsy Fernández-García, Briseida López-Guerra, Silio Gómez-Pascual, Jorge L. Cabrales-Fruto, Miguel affil: Centro de Investigaciones del Petróleo, Churruca no. 481 entre Vía Blanca y Washington, Cerro, La Habana, Código Postal 10200, Cuba su: Brass tubes Corrosion & anti-corrosives Brass Ammonia Strains & stresses (Mechanics) Liquefied petroleum gas sug: subj: Brass tubes Corrosion & anti-corrosives Brass Ammonia Strains & stresses (Mechanics) Liquefied petroleum gas keyword: ammonia brass corrosion failure stresses amoniaco corrosión falla latón tensiones ab: Premature failure of a condenser of an oil refinery was analyzed in order to determine its cause. A liquid petroleum gas polluted with ammonia and sulfides and cyanides ions flows outside of these tubes visual inspection in the fault zone showed cracks in circumferential direction of the tube and close to the plate showing bores. A dribble of seawater through the cracks, which flows inside the tubes was observed. By Multichannel Digital Emission Spectrometry it was determined that the alloy corresponds to an aluminum-brass structure of an solid disolution of zinc in copper. An increase in size and texture of the grains was observed by metallographic, analysis defining stress concentration on the fault zone. The hardness of 84 HB in the fault zone exceeds the value of 75 HB of a new tube from the same origin, which shows a plastic deformation. The X-Ray Diffraction pattern showed copper sulfides and copper and zinc hydroxysulphates as majority phases in the deposits, which point out the interaction of sulfate ions present in seawater with corrosive deposits. The condensed fluid was characterized by analytical techniques and showed a pH of 8, 26, conductivity of 51 mS/cm and concentration of chloride (51, 6 mg/L), sulfur (227,4 mg/L) and ammonium ions (1,96 mg/L) that place it as a highly corrosive medium. The presence of ammonia in the condensate fluid and internal tensions in the alloy created the conditions to arising the failure by stress corrosion cracking mechanism. Se analizó la falla prematura en un condensador de una refinería de petróleo con el objetivo de determinar su causa. Por el exterior de sus tubos circula gas licuado de petróleo contaminado con amoníaco e iones sulfuro y cianuro. Mediante inspección visual se encontraron grietas en sentido circunferencial de los tubos y próximas a la placa donde fueron mandrilados. A través de estas grietas fue observado un goteo del agua de mar que fluye por el interior de los tubos. Por Espectrometría Multicanal Digital de Emisión, se determinó la composición química de los tubos que se corresponde con el latón de aluminio de estructura monofásica α. El análisis metalografíco en la zona de falla mostró un aumento del tamaño y textura de los granos que definen concentración de tensiones. La dureza de 84 HB medida en la zona de falla supera los 75 HB de un tubo nuevo, que demuestra una deformación plástica. El difractograma de Rayos X de los depósitos de corrosión indicó sulfuros de cobre e hidroxisulfatos de cobre y cinc como fases mayoritarias, que evidenciaron la interacción de los iones sulfato del agua de mar con estos depósitos. La caracterización del condensado por técnicas analíticas arrojó un pH de 8,26, conductividad de 51 mS/cm, así como concentraciones de iones cloruro (51,6 mg/L), sulfuro (227,4 mg/L) y amonio (1,96 mg/L) que lo sitúan como un medio marcadamente corrosivo. La presencia de amoníaco en el condensado y tensiones internas en el latón, son premisas que originaron la falla por una corrosión bajo tensión. pubtype: Academic Journal doctype: Article src: R language: Spanish refInfo: copyright: @attributes: flag: Y custom: Copyright of Revista CENIC Ciencias Quimicas is the property of Centro Nacional de Investigaciones Cientificas and its content may not be copied or emailed to multiple sites without the copyright holder's express written permission. Additionally, content may not be used with any artificial intelligence tools or machine learning technologies. However, users may print, download, or email articles for individual use. item: Revista CENIC Ciencias Quimicas holder: Centro Nacional de Investigaciones Cientificas dt: @attributes: year: 2013 holdings: @attributes: islocal: N |
|---|