Multilayer zirconia: Influence of positioning within blank and sintering conditions on the in vitro performance of 3-unit fixed partial dentures.
Multilayer zirconia blanks comprise material layers with different optical and mechanical properties. Whether positioning within the blank, as well as variation in the sintering procedure, will lead to restorations with different properties is unclear. The purpose of this in vitro study was to test...
| Publicado en: | Journal of Prosthetic Dentistry Vol. 127; no. 1; pp. 141 - 146 |
|---|---|
| Autores principales: | , , , |
| Formato: | research Journal Article |
| Publicado: |
Elsevier B.V.
Jan2022
|
| Acceso en línea: | Ver este registro en EBSCOhost |
| fields | @attributes: recordID: 1 pdfLink: plink: https://search.ebscohost.com/login.aspx?direct=true&db=ccm&AN=154592465&site=ehost-live header: @attributes: shortDbName: ccm uiTerm: 154592465 longDbName: CINAHL Complete uiTag: AN controlInfo: bkinfo: dissinfo: jinfo: jid: 00223913 1ZB jtl: Journal of Prosthetic Dentistry issn: 00223913 maglogo: N pubinfo: dt: Jan2022 vid: 127 iid: 1 pid: 467 pub: Elsevier B.V. place: New York, New York artinfo: ui: 154592465 154592465 154592465 10.1016/j.prosdent.2020.11.009 154592465 ppf: 141 ppct: 5 formats: tig: atl: Multilayer zirconia: Influence of positioning within blank and sintering conditions on the in vitro performance of 3-unit fixed partial dentures. aug: au: Rosentritt, Martin Preis, Verena Schmid, Alois Strasser, Thomas affil: Professor, Department of Prosthetic Dentistry, UKR University Hospital Regensburg, Regensburg, Germany sug: subj: Denture, Partial, Fixed Methods Dental Restoration, Temporary Methods Metals, Heavy Dental Materials Materials Testing Human Molar In Vitro Studies Treatment Outcomes Evaluation Acrylic Resins Dental Prosthesis Design Models, Anatomic Dental Cements Dental Bonding Water Mechanics Tooth Fractures Prosthesis Failure One-Way Analysis of Variance Post Hoc Analysis Heat ab: Multilayer zirconia blanks comprise material layers with different optical and mechanical properties. Whether positioning within the blank, as well as variation in the sintering procedure, will lead to restorations with different properties is unclear. The purpose of this in vitro study was to test the influence of sintering procedures and positioning in a multilayer blank on the in vitro performance of 3-unit zirconia fixed partial dentures. Human molars were embedded in acrylic resin and prepared for 3-unit fixed partial dentures. Anatomic contour prostheses were milled from zirconia blanks (ZirCAD Prime 16 mm) in 3 different positions: above (cusp-top at the top of the blank), central (center of the prosthesis in the center of the blank), and bottom (margins at the lower edge of the blank). Sintering time (2:26, 4:25, 9:50 hours:minutes) was varied for the central and bottom prostheses. All prostheses were glazed and adhesively bonded. Thermocycling and mechanical loading was performed at 2×3000×5 °C/55 °C in distilled water for 1.2×106 cycles at a 50-N load. Then, fracture force was determined with a universal testing device by using central loading, a Ø12-mm steel ball, a 1-mm tin foil, and a rate of 1 mm/min. Failure was defined as 10% force drop or acoustic signal (crack). Statistical analysis was performed with 1-way ANOVA and Bonferroni correction (α=.05). All fixed partial dentures survived thermocycling and mechanical loading. Fracture forces varied between 1002 ±446 N (above; 9:50 hours) and 1760 ±607 N (central; 9:50 hours). The 1-way ANOVA revealed no statistically significant differences (P=.059) among the groups. Individual significant differences (P=.048) were found between prostheses from positions above, 9:50 hours, and central, 9:50 hours. For normal and long sintering times, fracture forces were highest in the central position. The sintering process and positioning of restorations within a multilayer zirconia blank have little effect on the mechanical properties of the prostheses. pubtype: Academic Journal doctype: research Journal Article ougenre: Article language: English refInfo: holdings: @attributes: islocal: N |
|---|