Efecto de la razón Zr/Ti sobre las propiedades de la cerámica PZT modificada con 0.05 mol de estroncio.
Ceramics corresponding to the lead titanate zirconate (PZT) ceramic system modified with strontium in different regions of phase diagram (Zr/Ti = 20/80, 40/60, 53/47, 60/40), were sinterized at 1290 °C for 70 minutes, the optimal sintering regimen according to previous studies. Tetragonal and romboh...
| Publicado en: | Revista Cubana de Física Vol. 26; no. 2A; pp. 174 - 179 |
|---|---|
| Autores principales: | , , , |
| Formato: | Artículo |
| Publicado: |
Universidad de La Habana
2009
|
| Materias: | |
| Acceso en línea: | Ver este registro en EBSCOhost |
| fields | @attributes: recordID: 1 pdfLink: plink: https://search.ebscohost.com/login.aspx?direct=true&db=lth&AN=73882111&site=ehost-live header: @attributes: shortDbName: lth uiTerm: 73882111 longDbName: MedicLatina uiTag: AN controlInfo: bkinfo: jinfo: jid: 02539268 UEW jtl: Revista Cubana de Física issn: 02539268 maglogo: N pubinfo: dt: 2009 vid: 26 iid: 2A pid: 21208 pub: Universidad de La Habana artinfo: ui: 73882111 ppf: 174 ppct: 5 formats: fmt: @attributes: type: P size: 685KB tig: atl: Efecto de la razón Zr/Ti sobre las propiedades de la cerámica PZT modificada con 0.05 mol de estroncio. aug: au: Costa, J. Suárez, A. Saniger, J. Calderón, F. affil: Instituto Cibernética, Matemáticas y Física, Ciudad de La Habana, Cuba CCADET, UNAM, Circ. Exterior s/n, A.P. 70-186 Ciudad Universitaria, C.P. 04510 México D.F. Facultad de Física/Instituto de Ciencias y Tecnología de Materiales, San Lázaro y L, Universidad de la Habana, 10400, Cuba su: Phase diagrams Lead zirconate titanate Sintering Strontium Curie temperature Piezoelectric ceramic testing sug: subj: Phase diagrams Lead zirconate titanate Sintering Strontium Curie temperature Piezoelectric ceramic testing keyword: 61.05.C- 77.84.Dy 78.20.Ci Cerámicas PZT constante dieléctrica rayos x ab: Ceramics corresponding to the lead titanate zirconate (PZT) ceramic system modified with strontium in different regions of phase diagram (Zr/Ti = 20/80, 40/60, 53/47, 60/40), were sinterized at 1290 °C for 70 minutes, the optimal sintering regimen according to previous studies. Tetragonal and rombohedral phases were obtained (mixed rombohedral and tetragonal were obtained for Zr/Ti = 53/47). As the Zr/Ti ratio increases, tetragonality and Curie temperature decreases, while the grain size did not show a noticeable variation. Our samples showed normal ferroelectric/ paraelectric transitions and a Curie-Weiss behaviour above transition temperature. Las cerámicas correspondientes al sistema cerámico titanato circonato de plomo (PZT) modificado con estroncio en diferentes regiones del diagrama de fase (Zr/Ti = 20/80, 40/60, 53/47, 60/40), fueron sinterizadas a 1290 °C durante 70 minutos, régimen óptimo de sinterización según estudios anteriores. Se obtuvo fase tetragonal y romboédrica (la Zr/Ti = 53/47 presentó mezcla de fase tetragonal y romboédrica). Con el aumento de la relación Zr/Ti la tetragonalidad y la temperatura de Curie decrecen, mientras que el tamaño de grano no mostró variación notable. Las muestras presentaron transición de fase ferroeléctrica-paraeléctrica de tipo normal, mostrando un comportamiento de Curie-Weiss por encima de la transición. pubtype: Academic Journal doctype: Article src: R language: Spanish refInfo: copyright: @attributes: flag: Y custom: Copyright of Revista Cubana de Física is the property of Universidad de La Habana and its content may not be copied or emailed to multiple sites without the copyright holder's express written permission. Additionally, content may not be used with any artificial intelligence tools or machine learning technologies. However, users may print, download, or email articles for individual use. item: Revista Cubana de Física holder: Universidad de La Habana dt: @attributes: year: 2009 holdings: @attributes: islocal: N |
|---|